The Difference of Aging for Materials by Thermal Analysis

Application Note TA5006

Introduction 

Sometimes chemical or physical properties of a material change due to aging. Thermal analysis is useful for quality control or to determine if properties have changed by confirming the differences of properties with material aging.

Instrument: TG-DTA8121 

The horizontal differential triple-coil balance system boasts a proven track record for mass-change measurements. It corrects or cancels various types of fluctuations that can be cause drifts. Combined with the newly developed electric circuits, it achieves low noise and excellent baseline stability. 

Measurement and analysis 

TG-DTA measurement result is shown Figure 1 . At 400℃, the original sample, taken from a hermetically sealed state, shows a mass loss of -22.7% with endothermic peaks due to dehydration.

On the other hands at 400℃, the sample kept at 25℃, 60% RH condition for 7 days reveals a small amount of mass loss of -9.7% due to dehydration, and then the mass loss is observed -25.8% at 600℃. Thisindicates that keeping the sample at 25℃, 60% RH for 7 days allowed the sample to absorb CO₂ from the air and that a part of Ca(OH)₂ changed to CaCO₃. Thus, only a small amount of mass loss due to dehydration is observed at 400℃ while the mass loss at 600℃ is the result of CaCO₃ decarbonation.

Also, the measurement result of the original exhibits a slight mass loss of -1.3% at 600℃, which suggesting that carbonation progressed in the some parts of the sample during storage.  

TA-5006 Figure 1 TG-DTA measurement results

Figure 1: TG-DTA measurement result of original (blue line) and  sample kept at 25℃, 60% RH condition for 7 days (red line) for Ca(OH)₂.  