In-plane pole figures on a steel sample

Background

In many cases, crystallographic texture (preferred orientation) can be introduced into a material during the fabrication process. For example, when steel sheets are rolled in the manufacturing process, a sheet texture is often produced. Since texture can affect a material's properties by introducing structural anisotropy, it is desirable to measure a material's texture. The typical measurement to determine texture is called a pole figure. Traditional pole figure measurements are made by recording the intensity of a given Bragg reflection as a function of rotation and tilt of the sample. In an in-plane pole figure, the incident beam, sample rotation, and detector angle are all moved, eliminating the necessity to tilt the sample. The in-plane pole figure also allows a greater range of texture to be recorded, as it now contains the in-plane (sample surface) texture of the sample.

Investigation

Figure 1 shows an in-plane pole figure of the <211> reflection for a rolled steel sheet sample collected on Rigaku's Ultima IV multipurpose diffraction system. The central dark red portion indicates texture along the [211] direction. The figure shows the pole figure in both in stereographic projection (contour map) and 3D display.

in-plane pole figure
Figure 1.